Confined growth of porous nitrogen-doped cobalt oxide nanoarrays as bifunctional oxygen electrocatalysts for rechargeable zinc–air batteries
Wang X, Liao Z, Fu Y, Neumann C, Turchanin A, Nam G, Zschech E, Cho J, Zhang J, Feng X (2020)
Publication Type: Journal article
Publication year: 2020
Journal
Book Volume: 26
Pages Range: 157-164
DOI: 10.1016/j.ensm.2019.12.043
Abstract
Cobalt oxides are promising bifunctional oxygen electrocatalysts due to their intrinsic activities toward both dissociation and formation of oxygen molecules. Unfortunately, their practical utilization is seriously hindered by the limited accessible active sites and inferior activity. Herein, vertically-aligned porous nanoarrays composed of ultrafine nitrogen-doped cobalt oxide (NP-Co3O4) nanoparticles (4-5 nm) are in-situ fabricated on carbon cloth (CC) via mild oxidation of Co-based zeolitic-imidazolate-framework (Co-ZIF) nanoarrays. The oxidation decomposition of 2-methylimidazolate ligands between Co nodes not only confines the growth of cobalt oxides, but also provides the nitrogen sources for realizing low-temperature (200 °C) nitrogen doping. In alkaline electrolyte, the as-built NP-Co3O4/CC manifests an extremely high oxygen reduction reaction (ORR) half-wave potential of ~0.9 V and a decreased oxygen evolution reaction (OER) overpotential of 330 mV at 10 mA cm−2, displaying a record low potential gap of 0.66 V. As bifunctional oxygen electrodes in rechargeable aqueous and all-solid-state flexible zinc-air batteries, the NP-Co3O4/CC-based batteries exhibit ultrahigh power densities up to 200 mW cm−2 and 99.8 mW cm−3, respectively, which are much higher than those of reported bifunctional oxygen electrocatalysts. This work paves a new avenue for the fabrication of porous nitrogen doped metal oxides towards high-performance zinc-air batteries.
Involved external institutions
How to cite
APA:
Wang, X., Liao, Z., Fu, Y., Neumann, C., Turchanin, A., Nam, G.,... Feng, X. (2020). Confined growth of porous nitrogen-doped cobalt oxide nanoarrays as bifunctional oxygen electrocatalysts for rechargeable zinc–air batteries. Energy Storage Materials, 26, 157-164. https://doi.org/10.1016/j.ensm.2019.12.043
MLA:
Wang, Xia, et al. "Confined growth of porous nitrogen-doped cobalt oxide nanoarrays as bifunctional oxygen electrocatalysts for rechargeable zinc–air batteries." Energy Storage Materials 26 (2020): 157-164.
BibTeX: Download